Polar Polystyrene Copolymers for Enhanced Foaming

ABSTRACT

A method of making a foamable polystyrene composition includes combining a styrenic monomer and a co-monomer containing a polar functional group to obtain a mixture, subjecting the mixture to polymerization to obtain a styrenic co-polymer, and combining the styrenic co-polymer with a blowing agent in a foaming process to obtain foamed articles.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a non-provisional of U.S. Provisional ApplicationSer. No. 61/441,389 filed Feb. 10, 2011.

FIELD

The present invention is generally related to polymeric compositions.More specifically, the present invention is related to foamablepolystyrene compositions.

BACKGROUND

Styrene, also known, as vinyl benzene, is an aromatic compound that isproduced in industrial quantities from ethylbenzene. The most commonmethod of styrene production comprises the dehydrogenation ofethylbenzene, which produces a crude product of styrene monomer andunreacted ethylbenzene and hydrogen. Polystyrene is an aromatic polymerproduced from the styrene monomer. Polystyrene is a widely used polymerfound in insulation, packaging, and disposable cutlery.

Different types of polystyrene materials can include general-purposepolystyrene (GPPS), high impact polystyrene (HIPS), and transparentimpact polystyrene (TIPS). Many conditions affect the properties of theresulting product, including processing time, temperature, pressure,purity of the monomer feedstock, and the presence of additives or othercompounds. These and other processing conditions alter the physical andchemical properties of the polystyrene product, affecting thesuitability for a desired use.

Foamed polystyrene offers the advantages of low cost and high structuralstrength for its density. A typical polystyrene foam also has arelatively high impact resistance and possesses excellent electrical andthermal insulation characteristics. Foamed polystyrene is useful in avariety of applications such as insulation, packaging, coolers, foodpackaging, decorative pieces, and dunnage. Additionally, polystyrenefoams are commonly classified into three general categories: lowdensity, medium density, and high density. Low density polystyrene foamsusually have a density of from about 1 to about 3 lb/ft³ whereas mediumdensity foams may have a density ranging from about 4 to about 19 lb/ft³and high density foams often have a density ranging from 20 to about 30lb/ft³.

The two main types of polystyrene foam are extruded polystyrene (XPS)foam and expanded polystyrene (EPS) foam. Extruded polystyrene foam istypically formed by mixing polystyrene with additives and blowing agentsinto an extruder that heats the mixture. The mixture is then extruded,foamed to the desired shape, and cooled. Expanded polystyrene foam istypically formed by expanding solid polystyrene beads containing ablowing agent such as pentane with steam or hot gas. These pre-expandedbeads may later be molded into the desired shape and expanded again withsteam or hot gas to fuse the beads together.

In the production of foamed polystyrene, it is common to utilize blowingagents such as methyl chloride, ethyl chloride, chlorocarbons,fluorocarbons (including HFCs) and chlorofluorocarbons (CFCs). However,such blowing agents have been heavily regulated due to potentialenvironmental impact. Many of these traditional and current physicalblowing agents are halogenated compounds, which demonstrate a highsolubility in polar polymers. An ongoing trend in foaming processdevelopment is to find environmentally benign chemicals as blowingagents. Some foaming processes have been using carbon dioxide (CO₂) asthe blowing agent or co-blowing agent. The advantages of using CO₂include low cost, minimal environmental impact, and eliminatingpotential fire hazards. It has therefore been desirable to use carbondioxide as a blowing agent from both environmental and economicstandpoints.

However, carbon dioxide has presented problems when used as a blowingagent. Carbon dioxide has been found to have a relatively low solubilityin styrenic polymer melts. For example, the solubility of CO₂ inpolystyrene is only ca. 4 wt % at 6.5 MPa and 373 K, as measured byYoshiyuki Sato et. al. (Journal of Supercritical Fluids 2001, 19,187-198.). The low solubility results in high extrusion pressures, whichincreases costs and reduces quality. The low solubility also results ina higher density product. It would be desirable to obtain a polystyreneproduct having a high carbon dioxide solubility in order to reduce costsand increase product quality.

Furthermore, carbon dioxide has relatively higher vapor pressure anddiffusivity, compared to halogenated blowing agents. In the extrusionfoaming process using CO2 as the blowing agent, the melt strength ofpolystyrene is often inadequate, which leads to immature bubblebreakage/coalescence, non-uniform cell morphology, and excessive opencell content. It would be desirable to obtain a polystyrene resin havingimproved melt strength in order to perform well in foaming processes.

SUMMARY

An embodiment of the present invention is a polystyrene product that isa styrenic co-polymer resulting from polymerization of a reactionmixture of a styrenic monomer and co-monomers having polar functionalgroups. The polystyrene can then be used in an extrusion foaming processwith the presence of blowing agents.

In a non-limiting embodiment, either by itself or in combination withany other aspect of the invention, the styrenic monomer can be selectedfrom the group consisting of styrene, alpha-methyl styrene, vinyltoluene, p-methyl styrene, t-butyl styrene, o-chlorostyrene, vinylpyridine, and any combinations thereof, and can be present in amountsranging from 80 to 99.9 wt % based on the total weight of the expandablepolystyrene.

In a non-limiting embodiment, either by itself or in combination withany other aspect of the invention, the co-monomer can be selected fromthe group consisting of hydroxyethylmethacrylate (HEMA), caprolactoneacrylate, alkyl (meth)acrylate, fluorinated (meth)acrylate and any otherpolymerizable monomers containing esters, ethers, carboxylic acids orsilanes, and combinations thereof, and can be present in amounts rangingfrom 0.5 to 20 wt % based on the total weight of the reaction mixture.

In a non-limiting embodiment, either by itself or in combination withany other aspect of the invention, the blowing agent can be carbondioxide (CO₂), water (H₂O), ethanol, air, nitrogen, argon, and heliumand combinations thereof and can be present in the styrenic co-polymerin a weight proportion ranging from 1 to 30 parts per 100 parts ofstyrenic material.

In a non-limiting embodiment, either by itself or in combination withany other aspect of the invention, the present invention includes anyarticle made from the polystyrene of any embodiment disclosed herein.

Other possible embodiments include two or more of the above aspects ofthe invention. In an embodiment the method includes all of the aboveaspects and the various procedures can be carried out in any order.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a graph illustrating polylactic acid (PLA) particle sizedistribution from PLA blends with various polystyrene copolymers.

FIG. 2 is a graph illustrating PLA particle size distribution from PLAblends modified with styrene-maleic anhydride (SMA).

FIG. 3 is a graph of results from haul-off melt strength tests atvarious HEMA concentrations.

FIG. 4 is a diagram illustrating the experimental scheme of dynamicgravimetric measurement of CO₂ solubility.

FIG. 5 is a graph of CO₂ desorption versus CO₂ solubility.

FIG. 6 is a graph of CO₂ desorption versus normalized CO₂ solubility.

DETAILED DESCRIPTION

The present invention includes styrenic polymers and polymer blends. Inan embodiment, the present invention includes styrenic copolymers ofstyrene and a second monomer containing a polar functional group. In amore specific embodiment, the present invention includes a foamablepolymeric composition containing such styrenic copolymers.

In an embodiment, the present invention includes a styrenic polymer. Inanother embodiment, the styrenic polymer includes polymers ofmonovinylaromatic compounds, such as styrene, alpamethyl styrene andring-substituted styrenes. In an alternative embodiment, the styrenicpolymer includes a homopolymer and/or copolymer of polystyrene. Styrenicmonomers for use in the styrenic polymer composition can be selectedfrom the group of styrene, alpha-methyl styrene, vinyl toluene, t-butylstyrene, o-chlorostyrene, vinyl pyridine, and any combinations thereof.The styrenic polymeric component in the blend of the present inventioncan be produced by any known process.

The styrenic polymer of the present invention may includegeneral-purpose polystyrene (GPPS), high-impact polystyrene (HIPS),styrenic copolymer compositions, or any combinations thereof. In anembodiment, the HIPS contains an elastomeric material. In an embodiment,the HIPS contains an elastomeric phase embedded in the polystyrenematrix, which results in the polystyrene having an increased impactresistance.

The blend of the present invention may contain any desired amounts of astyrenic polymer. In an embodiment, the blend contains at least 50 wt %of a styrenic polymer. In another embodiment, the blend contains astyrenic polymer in amounts ranging from 1 to 99 wt %, 50 to 95 wt %, 60to 92 wt %, and optionally 70 to 90 wt %. In a further embodiment, theblend contains a styrene polymer in amounts ranging from 80 to 99 wt %.In an even further embodiment, the blend contains a styrenic polymer inamounts ranging from 90 to 95 wt %.

The styrenic polymer of the present invention may be formed byco-polymerizing a first monomer with a second monomer. The first monomerand the second monomer may be co-polymerized by having the first monomerand the second monomer present in a reaction mixture that is subjectedto polymerization conditions. The first monomer may includemonovinylaromatic compounds, such as styrene, alpha-methyl styrene andring-substituted styrenes. In an embodiment, the first monomer isselected from the group of styrene, alpha-methyl styrene, vinyl toluene,t-butyl styrene, o-chlorostyrene, vinyl pyridine, and any combinationsthereof. In another embodiment, styrene is used exclusively as the firstmonomer. In an embodiment, the first monomer is present in the reactionmixture in amounts of at least 50 wt % of the reaction mixture. Inanother embodiment, the first monomer is present in the reaction mixturein amounts ranging from 80 to 99.9 wt % of the reaction mixture. In afurther embodiment, the first monomer is present in the reaction mixturein amounts ranging from 90 to 99 wt %. Embodiments of the second monomercan be any suitable monomer capable of polymerization to form a styreniccopolymer. Examples of suitable second monomers can includehydroxyethylmethacrylate, caprolactone acrylate, alkyl (meth)acrylate,fluorinated (meth)acrylate and any other polymerizable monomerscontaining polar functionalities such as esters, ethers, carboxylicacids or silanes, and combinations thereof.

Embodiments of the present invention include at least one second monomercontaining a polar functional group. The second monomer containing apolar functional group may also be referred to herein as a “polarmonomer”. In an embodiment, the polar monomer is a polar vinylfunctional monomer. In another embodiment, the polar monomer is selectedfrom the group of hydroxyethylmethacrylate, caprolactone acrylate, alkyl(meth)acrylate, fluorinated (meth)acrylate and any other polymerizablemonomers containing polar functionalities such as esters, ethers,carboxylic acids or silanes, and combinations thereof. In a furtherembodiment, the polar monomer is selected from the group of caprolactoneacrylate, polyvinyl acetate, and HEMA, and combinations thereof. In aneven further embodiment, the polar monomer is HEMA. In anotherembodiment the second monomer may be selected from the group of, maleicanhydride (MAH), butyl acrylate, butyl methacrylate, and combinationsthereof.

The styrenic polymer of the present invention may be prepared bypolymerizing a reaction mixture containing a first monomer and a secondmonomer having a polar functional group. The first monomer and secondmonomer may be present in the reaction mixture in any desired amounts.In an embodiment, the second monomer is present in the reaction mixturein amounts of at least 0.1 wt % of the reaction mixture. In anotherembodiment, the second monomer is present in the reaction mixture inamounts of less than 20 wt % of the reaction mixture. In an alternativeembodiment, the second monomer is present in the reaction mixture inamounts ranging from 1 to 20 wt %. In a further embodiment, the secondmonomer is present in the reaction mixture in amounts ranging from 1 to10 wt %. In an even further embodiment, the second monomer is present inthe reaction mixture in amounts ranging from 1 to 5 wt %.

The polymerization of the styrenic monomer and the polar co-monomer maybe carried out using any method known to one having ordinary skill inthe art or performing such polymerizations. In an embodiment, thepolymerization may be carried out by using a polymerization initiator.In an embodiment, the polymerization initiators include but are notlimited to perketals, hydroperoxides, peroxycarbonates and the like. Inanother embodiment, the polymerization initiators may be selected fromthe group of benzoyl peroxide, lauroyl peroxide, t-butyl peroxybenzoate,and 1,1-di-t-butylperoxy-2,4-di-t-butylcycleohexane, and combinationsthereof. In an embodiment, the amount of the polymerization initiator isfrom 0.01 to 1.0 wt % of the reaction mixture. In another embodiment,the amount of the polymerization initiator is from 0.01 to 0.5 wt % ofthe reaction mixture. In a further embodiment, the amount of thepolymerization initiator is from 0.025 to 0.05 wt % of the reactionmixture.

Any process capable of processing or polymerizing styrenic monomers maybe used to prepare the styrenic co-polymer of the present invention. Inan embodiment, the polymerization reaction to prepare the styrenicco-polymer may be carried out in a solution or mass polymerizationprocess. Mass polymerization, or bulk polymerization, refers to thepolymerization of a monomer in the absence of any medium other than themonomers and a catalyst or polymerization initiator. Solutionpolymerization refers to a polymerization process in wherein themonomers and polymerization initiators are dissolved in a non-monomericliquid solvent at the beginning of the polymerization reaction.

The polymerization may be either a batch process or a continuousprocess. In an embodiment, the polymerization reaction may be carriedout using a continuous production process in a polymerization apparatusincluding a single reactor or multiple reactors. The styrenic polymercomposition can be prepared using an upflow reactor, a downflow reactor,or any combinations thereof. The reactors and conditions for theproduction of a polymer composition, specifically polystyrene, aredisclosed in U.S. Pat. No. 4,777,210, which is incorporated by referenceherein in its entirety.

The temperature ranges useful in the polymerization process of thepresent disclosure can be selected to be consistent with the operationalcharacteristics of the equipment used to perform the polymerization. Inan embodiment, the polymerization temperature ranges from 90 to 240° C.In another embodiment, the polymerization temperature ranges from 100 to180° C. In yet another embodiment, the polymerization reaction may becarried out in multiple reactors in which each reactor is operated underan optimum temperature range. For example, the polymerization reactionmay be carried out in a reactor system employing a first polymerizationreactor and a second polymerization reactor that may be eithercontinuously stirred tank reactors (CSTR) or plug-flow reactors. In anembodiment, a polymerization process for the production of a styrenicco-polymer of the type disclosed herein containing multiple reactors mayhave the first reactor (e.g., a CSTR), also referred to as aprepolymerization reactor, operated under temperatures ranging from 90to 135° C. while the second reactor (e.g. CSTR or plug flow) may beoperated under temperatures ranging from 100 to 165° C.

In an alternative embodiment, the co-polymer may be obtained bypolymerization in which heat is used as the initiator. In a furtherembodiment, the co-polymer may be prepared using a non-conventionalinitiator such as a metallocene catalyst as is disclosed in U.S. Pat.No. 6,706,827 to Lyu, et al., which is incorporated herein by referencein its entirety. In one embodiment, the monomers may be admixed with asolvent and then polymerized. In another embodiment, one of the monomersis dissolved in the other and then polymerized. In still anotherembodiment, the monomers may be fed concurrently and separately to areactor, either neat or dissolved in a solvent, such as mineral oil. Inyet another embodiment, the second monomer may be prepared in-situ orimmediately prior to the polymerization by admixing the raw materialcomponents, such as an unsaturated acid or anhydride and a metalalkoxide, in-line or in the reactor. Any process for polymerizingmonomers having polymerizable unsaturation know to be useful to those ofordinary skill in the art in preparing such polymers may be used. Forexample, the process disclosed in U.S. Pat. No. 5,540,813 to Sosa, etal., may be used and is incorporated herein by reference in itsentirety. The processes disclosed in U.S. Pat. No. 3,660,535 to Finch,et al., and U.S. Pat. No. 3,658,946 to Bronstert, et al., may be usedand are both incorporated herein by reference in their entirety. Anyprocess for preparing general purpose polystyrene may be used to preparethe styrenic co-polymer of the present invention.

In certain embodiments, the styrenic copolymer may be admixed withadditives prior to being used in end use applications. For example, thestyrenic copolymer may be admixed with additives that include withoutlimitation, antioxidants, UV stabilizers or absorbents, lubricants,plasticizers, ultra-violet screening agents, oxidants, anti-staticagents, fire retardants, processing oils, mold release agents, fillers,pigments/dyes, coloring agents, and other similar compositions. Anyadditive known to those of ordinary skill in the art to be useful in thepreparation of styrenic copolymers may be used. CO₂ solubility mayincrease for lower molecular weight polystyrene copolymer, therefore, itwould be desirable to maintain or control the molecular weight of thestyrenic copolymer. In an embodiment, chain transfer agents and/ordiluents may be added before and/or during polymerization in order tohelp control the molecular weight of the resulting styrenic copolymer.

The obtained polystyrene copolymer may then be sent to an extruder orother step to obtain an end use article. The blowing agents such as HFCor CO₂ can be added into the polymer during the extrusion process.

In an embodiment, styrene monomer is combined with a polar comonomer anda plasticizer and subsequently polymerized to form a polar polystyrenecopolymer. The polar polystyrene copolymer can then be sent to anextruder or other step to obtain an end use article. The blowing agentsare added to the polystyrene containing composition during the extrudingstep.

In an embodiment, styrene monomer is combined with a second polarmonomer and subsequently polymerized to form a polystyrene copolymer. Inan embodiment, the polystyrene copolymer is sent to an extruder or otherstep to obtain an end use article. The blowing agents are added to thepolystyrene containing composition during the extruding step.

The present invention may include foamed articles which may be formed bymelting and mixing the styrenic copolymer of the invention to form apolymer melt, incorporating a blowing agent into the polymer melt toform a foamable blend, and extruding the foamable blend through a die toform the foamed structure. During melting and mixing, the polymericmaterial may be heated to a temperature at or above the glass transitiontemperature of the polymeric material. The melting and mixing ofpolymeric material and any additives may be accomplished by any meansknown in the art, including extruding, mixing, and/or blending. In anembodiment, a blowing agent is blended with molten polymeric material.The blending of the blowing agent with the molten polymeric material maybe performed under atmospheric or elevated pressures.

In an embodiment, the blowing agent is incorporated into the styreniccopolymer in a weight proportion ranging from 1 to 30 parts per 100parts of the polymeric material to be foamed. In another embodiment, theblowing agent is incorporated into the styrenic copolymer in a weightproportion ranging from 2 to 18 per 100 parts per polymeric material tobe foamed. In a further embodiment, the blowing agent is incorporatedinto the styrenic copolymer in a weight proportion ranging from 4 to 12parts per 100 parts per polymeric material to be foamed.

The blowing agents of the present invention may include organic and/orinorganic compounds. In an embodiment, the blowing agents of the presentinvention are environmentally benign than methyl chloride, ethylchloride, chlorocarbons, fluorocarbons (including HFCs) andchlorofluorocarbons (CFCs). In a further embodiment, the blowing agentsof the present invention are selected from the group of carbon dioxide(CO₂), water (H₂O), ethanol, air, nitrogen, argon, butane, pentane, andhelium and combinations thereof. In an even further embodiment, theblowing agent of the present invention is entirely composed of CO₂.

The foamable blend may be cooled after the blowing agent is incorporatedinto the styrenic blend. In an embodiment, the foamable blend is cooledto temperatures ranging from 30 to 150° C., optionally 75 to 150° C. Thecooled foamable blend may then be passed through a die into a zone oflower pressure to form an article of foamed structure. The polystyrenecopolymer can be used for not only foams, but also rigid blends.

The obtained foamed polystyrene copolymer may have any desired density.In an embodiment, the density of the foamed polystyrene copolymer rangesfrom 15 to 0.1 lbs/ft³. In another embodiment, the density of the foamedpolystyrene copolymer ranges from 10 to 0.5 lbs/ft³. In a furtherembodiment, the density of the foamed polystyrene copolymer ranges from3 to 0.6 lbs/ft³.

An end use article may include a polystyrene copolymer of the presentinvention. In an embodiment, the articles include films and thermoformedor foamed articles. For example, a final article may be thermoformedfrom a sheet containing the polystyrene copolymer. In anotherembodiment, the end use articles include foamed articles, which may havea foamed structure. In an embodiment, an article can be obtained bysubjecting the polymeric composition to a plastics shaping process suchas extrusion. The polymeric composition may be formed into end usearticles including food packaging, food/beverage containers, polymericfoam substrate, foamed insulation, building insulation, protective headgear, toys, dunnage, and the like.

In an embodiment, the obtained polystyrene foam is a multicellulararticle having a plurality of cells that may be open or closed. Inanother embodiment, the majority of the cells are open. In analternative embodiment, the majority of the cells are closed.

EXAMPLES Example 1

A series of polystyrene samples were made with the addition of polarmodifiers as listed in Table 1 below. The polymerization reaction wascarried out in a CSTR-type batch reactor. Lupersol-233 was added as theinitiator with an initial concentration of about 170 ppm in the reactionmixture. The reaction was then run isothermally at 130° C. withcontinuous agitation at 150 rpm for about 3 hours or until 75%conversion was obtained. The reaction mixture was then transferred ontoan aluminum surface and devolatized under active vacuum of less than 10torr at 225° C. for 45 minutes.

The polar modifiers listed in Table 1 include styrene-maleic anhydride(SMA), a copolymer of styrene and maleic anhydride, which arecommercially available from Sartomer Company, Inc. SMA® 1000P, SMA®3000P and SMA® EF80 have styrene-to-maleic anhydride molar ratios of1:1, 3:1 and 8:1, respectively. The polar modifiers also include butylacrylate, butyl methacrylate, hydroxyethylmethacrylate (HEMA), andmaleic anhydride (MAH). The loading of modifiers is 5 wt %, except formaleic anhydride (MAH). The loading of MAH is limited to 3.5 wt % and,in a separate sample, 1.75 wt % due to its limited solubility instyrene. In Table 1, below, PDI represents polydispersity index whereinPDI=Mw/Mn, Tg₁ represents the first glass transition temperature and Tg₂represents a second glass transition temperature, if applicable.

TABLE 1 Characterization of Modified Polystyrene SMA 1000P Modifier None(1:1) SMA 3000P (3:1) SMA EF80 (8:1) wt % 0 5.0 5.0 5.0 mol(# of molesof 0 0.025 0.012 0.005 polar monomer unit)/(100 g of polymer)Transparency Clear Opaque Opaque Opaque Tg₁ 105.2 104.8 104.5 104.4 Tg₂n/a 169.3 n/a n/a Melt Flow Rate 2.1 2.2 2.8 2.9 Mn 130,000 138,000132,000 84,100 Mw 271,000 273,000 269,000 262,000 Mz 415,000 439,000418,000 417,000 PDI 2.1 2.0 2.0 3.1 Peak MW 259,000 255,000 259,000265,000 Butyl Butyl Modifier Acrylate Methacrylate HEMA MAH MAH wt % 5.05.0 5.0 1.75 3.5 mol(# of moles of 0.039 0.035 0.038 0.018 0.036 polarmonomer unit)/(100 g of polymer) Transparency Clear Clear Clear ClearSemi-clear Tg₁ 94.8 98.2 102.6 105.0 104.0 Tg₂ n/a n/a n/a n/a n/a MeltFlow Rate 3.3 2.9 1.7 2.2 3.3 Mn 136,000 122,000 128,000 115,000 97,300Mw 184,000 260,000 312,000 250,000 220,000 Mz 433,000 398,000 529,000391,000 350,000 PDI 2.1 2.1 2.4 2.2 2.3 Peak MW 271,000 250,000 270,000239,000 212,000

An indicator of polarity change in polystyrene is how well the materialblends with another polar polymer such as polylactic acid (PLA). In thisexperiment, the modified polystyrene samples above were blended with 5wt. % PLA 3251D (NatureWorks® Ingeo™) in a Haake mixer. The Haake mixerwas operated at a temperature of 210° C. under a nitrogen atmosphere for3 minutes with agitation speeds of 60 rpm. The size of the PLA particlesin the blends were evaluated by solution dynamic light scattering. Theblend samples were dispersed in methyl ethyl ketone (MEK), a goodsolvent for polystyrene but not for PLA. FIG. 1 and FIG. 2 show the PLAparticle size distribution from different polystyrene blends. FIG. 1compares polystyrene copolymerized with different comonomers. All of thepolystyrene copolymer samples show improved dispersion of PLA whencompared to crystal polystyrene, which suggests the polarity change inPS and better polar interaction with PLA. Use of HEMA in PS gave thebest result with a relatively narrower distribution peaked at particlesizes of 0.5 μm. Similar but slightly worse results were obtained withpolystyrene modified by butyl-acrylate/methacryates as well as maleicanhydride.

FIG. 2 compares polystyrene modified with different styrene-maleicanhydride copolymers (SMAs). The SMAs were incorporated into polystyreneduring batch reactions. The PLA particle size distributions from the SMAblends did not seem to improve much compared to unmodified PS. The SMAswere not as effective as polar comonomers, probably due to therelatively lower molar concentration of polar groups of SMAs under thesame weight percentage loading (see Table 1 above). In addition, theSMAs containing the higher percentage of maleic anhydride (such as 1000Pand 3000P) are less soluble in styrene. A miscible blend of GPPS and SMAwas only made with SMA EF80, which has a styrene-to-maleic anhydride of8:1 and contains the lowest concentration of maleic anhydride among thevarious SMAs used. FIG. 2 also shows that use of HEMA comonomer achievedthe best result with a relatively narrower particle size distributionpeaked at particle sizes of 0.5 μm.

Example 2

Hydroxyl functional polystyrene was prepared in a batch reaction processby copolymerizing styrene with 2-hydroxyethyl methacrylate (HEMA) atvaried concentrations ranging from 0 to 5 wt. % in the feed (see Table2). The polymerization reaction was carried out in a CSTR-type batchreactor. Lupersol-233 was added as the initiator with an initialconcentration of about 170 ppm in the reaction mixture. The reaction wasthen run isothermally at 130° C. with continuous agitation at 150 rpmfor about 3 hours or until 75% conversion was obtained. The reactionmixture was then transferred onto an aluminum surface and devolatizedunder active vacuum of less than 10 torr at 225° C. for 45 minutes.

TABLE 2 Feed Formulations in Batch Synthesis of HEMA-modifiedpolystyrene Run No. 1 2 3 4 Styrene (grams) 200 198 195 190 HEMA (grams)0 2 5 10 HEMA (wt. %) 0 1.0 2.5 5.0 TOTAL (grams) 200 200 200 200

The concentration effect of hydroxyl groups on polystyrene properties isshown in Table 3 below. It appears that the measured molecular weights(Mw and Mz) increase while the melt flow rate decreases as theconcentration of HEMA increases. The results suggest strengthenedinter-chain interactions among polystyrene chains, possible due to thepresence of polar interactions such as hydrogen bonding. The haul-offmelt strength tests were also conducted on the polystyrene samples. Aclear trend can be observed in FIG. 3, i.e., the melt strength of thematerial increases along with the concentration of HEMA. The improvementin the melt strength is desirable for foaming of polystyrene using CO₂as the blowing agent.

TABLE 3 Characterization of HEMA-modified polystyrene Mn Mw Mz PDI MFIHEMA (g · (g · (g · Mp Mw/ (g · 10 Tg (wt. %) mol⁻¹) mol⁻¹) mol⁻¹) (g ·mol⁻¹) Mn min⁻¹) (° C.) 0.0 129,000 269,000 408,000 260,000 2.1 2.2104.4 1.0 135,000 329,000 515,000 309,000 2.4 1.1~2.5 104.1 2.5 142,000336,000 523,000 315,000 2.4 1.9~2.3 103.2 5.0 127,000 355,000 584,000320,000 2.8 0.3 103.1

Example 3

Polymerization reactions were conducted to prepare PS copolymerscontaining different polar functional co-monomers. As described inearlier examples, the polymerization reaction was carried out in aCSTR-type batch reactor. Lupersol-233 was added as the initiator with aninitial concentration of about 170 ppm in the reaction mixture. Thereaction was then run isothermally at 130° C. with continuous agitationat 150 rpm for about 3 hours or until 75% conversion was obtained. Thereaction mixture was then transferred onto an aluminum surface anddevolatized under active vacuum of less than 10 torr at 225° C. for 45minutes.

The co-monomers used include 2-hydroxylethyl methacrylate (HEMA, 98%,CAS#868-77-9), glycidyl methacrylate (GMA, CAS#106-91-2), butylmethacrylate (Butyl MA, CAS#97-88-1), isodecyl methacrylate (IsodecylMA, CAS#29964-84-9), 2,2,3,4,4,4-hexafluorobutyl acrylate (Fluorinated,CAS#54052-90-3), 3-(trimethoxysilyl)propyl methacrylate (Silyl,CAS#2530-85-0), caprolactone acrylate (Caprolactone, CAS#110489-05-9),methoxy polyethylene glycol (350) monomethacrylate (PEG350-MA,CAS#26915-72-0) or methoxy polyethylene glycol (550) monomethacrylate(PEG550-MA, CAS#26915-72-0).

The solubility and diffusivity of CO₂ in the copolymers weresubsequently measured using the method described below. The results arelisted in Table 4, with other characterization data.

Example 4

Measurement of CO₂ Solubility The general scheme of measurement isillustrated in FIG. 4. Polymer samples were molded into disks with athickness of 1.4 mm and a diameter of 25 mm. The relatively largesurface area on both sides of the disks ensures that the diffusion ofgas occurs mainly in the normal direction of the disk planes. The sampledisk was weighed (M_(ini)) and then transferred into a Parr pressurevessel, which was purged with CO₂ at least 3 times, subsequently heatedto 50° C. and pressurized with carbon dioxide to 1,500 psi to reach asupercritical state. Both temperature and pressure were maintained for aperiod of time (t₃ in FIG. 4) to allow CO₂ absorption into the sampledisk. The pressure is then released instantaneously to atmosphere (att₄). The sample disk is quickly taken from the pressure vessel andplaced onto a moisture balance (Ohaus) to record the weight loss as afunction of time under ambient conditions. Reduction of sample weightwas observed due to desorption of CO₂. The dynamic evolution of weight(M_(t)) was recorded by a computer and WinWedge program. The dynamicweight change of the sample disk recorded (after t₅) was used tocalculate the CO₂ solubility as well as diffusivity with the aid ofFick's diffusion law and appropriate boundary conditions. The weightdata recorded (after t₅) can be extrapolated to the initial weight (att₄), prior to the depressurization, to obtain the CO₂ absorptionconcentration as well as the desorption rate of CO₂.

The amount of CO₂ remaining in the sample disk at any given moment canbe represented by M_(gas,t) and calculated according to equation:M_(gas,t)=(M_(t)−M_(ini))/M_(ini)X100%. The amount of CO₂ dissolved in asample under equilibrium conditions is M_(gas,t) at t=0, i.e., rightbefore the depressurization. M_(gas,t) should drop as a function of time(t) and eventually approach zero when t=∞.

To find the amount of CO₂ dissolved in the sample prior to thedepressurization, one needs to extrapolate the data to t=0. Assuming aconstant diffusion coefficient of CO₂, it can be shown from literaturethat M_(gas,t) is a linear function of the square root of time:

$\begin{matrix}{M_{{gas},t} = {M_{{gas},0} - {\frac{4}{l} \cdot \sqrt{\frac{D \cdot t}{\pi}} \cdot M_{{gas},0}}}} & \left( {{Equation}\mspace{14mu} 1} \right)\end{matrix}$

where l is the thickness of the sample disk and D is the diffusioncoefficient of CO₂. Use of this equation implicitly assumes uniformityof the initial gas concentration and homogeneity and isotropy of thesample structure. It also implies that the diffusion coefficient isconstant regardless of the desorption time, gas concentration in thesample during desorption and temperature variation which could existduring the depressurization process. By making a linear plot ofM_(gas,t) vs. t_(1/2), one can calculate M_(gas,0) and D from theintercept (at t=0) and slope, which corresponds to CO₂ solubility anddiffusivity in the sample polymer, respectively.

CO₂ Solubility in Modified PS Dynamic CO₂ solubility measurements wereconducted on an un-modified PS reference, commercialpoly(styrene-co-acrylonitrile) (SAN) and a series of polarity-modifiedPS lab samples. Table 4 below lists the results by the name ofco-monomers in the polystyrene copolymers. A plot of CO₂ diffusivityversus solubility of various samples was also constructed as shown inFIG. 5.

Compared to the un-modified polystyrene, SAN showed significantly higherCO₂ solubility (15.6%) and lower CO₂ desorption diffusivity (1.1×10⁻⁷cm²/s). The affinity of polar groups in SAN toward CO₂ may partiallyexplain, from an enthalpy point of view, the enhanced (thermodynamic)solubility and slowed (kinetic) diffusivity. The swelling in CO₂ wassmall (<5% in thickness) for both SAN and PS.

Besides SAN, it is clear that all the polarity-modified PS copolymersshow higher CO₂ solubility, more or less, when compared to theun-modified PS reference. The greatest CO₂ solubility enhancement wasobserved on 3-(trimethoxysilyl)propyl methacrylate-modified PS(Silyl-PS) with a 20% increase of solubility. This was followed by PScopolymerized with alkyl methacrylates or fluorinated acrylate. The factthat none of the samples has lower CO₂ solubility than the un-modifiedPS demonstrates the effectiveness of polarity-driven structuralmodification of PS for CO₂ solubility enhancement.

The high gas diffusivity is not desired for foaming processes as it hasa negative impact on cell morphology control and can lead to acceleratedgas exchange with air (foam aging). Among the different modified PStested, there appear to be a few copolymers which actually show lowerdiffusivity than the un-modified PS reference. Examples include HEMA-,alkyl methacrylate- and caprolactone-modified PS.

TABLE 4 CO₂ Solubility and Diffusivity in PS Copolymers (CO2 SoakingConditions: 1500 psi, 50° C.) Solubility Diffusivity Co-monomer (g per100 g (10⁻⁷ cm²sec⁻¹, MI Sample (wt. %) polymer) 25° C.) Swell % T_(g)(° C.) (g/10 min) Mn Mw Mz Mw/Mn Mp PS Ref. 0 10.1 2.8 5% 104 2.2129,000 269,000 308,000 2.1 260,000 SAN 25 15.6 1.1 4% 105   165000*HEMA 5.0 10.7 1.9 3% 103 0.3 127,000 355,000 584,000 2.8 320,000 HEMA2.5 11.0 2.6 7% 103 1.9 142,000 336,000 523,000 2.4 315,000 GMA 5.0 11.03.0 4% 101 2.4 125,000 277,000 435,000 2.2 261,000 Butyl MA 5.0 11.4 2.32% 98 2.9 122,000 260,000 398,000 2.1 250,000 Isodecyl MA 5.0 11.7 2.813% 94 3.0 141,000 362,000 668,000 2.6 273,000 Flurinated 5.0 11.7 3.012% 96 n/a 125,000 265,000 409,000 2.1 252,000 Silyl 2.5 10.2 3.5 6% 1012.6 128,000 298,000 493,000 2.3 260,000 Silyl 5.0 12.1 5.8 36% 97 n/a132,000 335,000 630,000 2.5 261,000 Caprolactone 2.5 10.8 2.2 9% 92 n/a139,000 522,000 1,144,000 3.8 248,000 PEG350 MA 5.0 11.4 n/a n/a 81 0.369,000 383,000 1,107,000 5.6 167,000 PEG550 MA 5.0 11.0 5.0 30% 80 4.4106,000 334,000 681,000 3.2 242,000

The measured CO₂ solubility data have indicated enhanced CO₂ solubilitywhen the polar co-monomers of various concentrations are incorporatedinto polystyrene. To compare the modifier efficiency in CO₂ solubilityimprovement, the portion of CO₂ solubility contributed by the co-monomerwas normalized based on the weight. The normalized data (Table 5 andFIG. 6) showed that the silyl methacrylate and HEMA were more effectiveto boost CO₂ solubility than other co-monomers. Interestingly,acrylonitrile had only moderate efficiency on CO₂ solubilityenhancement, comparable to isodecyl- and fluorinated acrylates.

TABLE 5 Normalized CO₂ Solubility and Diffusivity in PS Copolymers (CO2Soaking Conditions: 1500 psi, 50° C.) Solubility Diffusivity Co- (g per100 g Solubility Contribution- S_(CO2-extra)/Mass (10⁻⁷ cm²sec⁻¹, Samplemonomer(wt. %) polymer) Comonomer (S_(CO2-extra)) of Comonomer 25° C.)PS Ref. 0 10.1 0.0 0.10 2.8 SAN 25 15.6 8.0 3.32 1.1 HEMA 5.0 10.7 1.10.22 1.9 HEMA 2.5 11.0 1.2 0.46 2.6 GMA 5.0 11.0 1.4 0.28 3.0 Butyl MA5.0 11.4 1.8 0.36 2.3 Isodecyl MA 5.0 11.7 2.1 0.42 2.8 Flurinated 5.011.7 2.1 0.42 3.0 Silyl 2.5 10.2 0.4 0.14 3.5 Silyl 5.0 12.1 2.5 0.505.8 Caprolactone 2.5 10.8 1.0 0.38 2.2 PEG350 MA 5.0 11.4 1.8 0.36 n/aPEG550 MA 5.0 11.0 1.4 0.28 5.0

With both diffusivity and normalized solubility considered, thereappeared to be a few co-monomers which achieved a good balance ofdiffusivity and solubility. Examples included the caprolactone, butyland hydroxyethyl methacrylate modified PS. The CO₂ solubilityimprovement in these modified PS exceeded that in SAN while thediffusivity was well contained to be below that in the un-modified PS.Commercial SAN has a very low CO₂ diffusivity of 1.1×10⁻⁷ cm²/s, despiteits high CO₂ solubility.

Overall, the results clearly demonstrate that the presence of polargroups in polystyrene can lead to a higher CO₂ solubility. A CO₂solubility enhancement will benefit foaming of polystyrene using CO2 asthe blowing agent.

As used herein, the term “monomer” refers to a relatively simplecompound, usually containing carbon and of low molecular weight, whichcan react by combining one or more similar compounds with itself toproduce a polymer.

As used herein, the term “co-monomer” refers to a monomer that iscopolymerized with at least one different monomer in a copolymerizationreaction resulting in a copolymer.

As used herein, the term “homopolymer” refers to a polymer resultingfrom polymerization of a single monomer species.

As used herein, the term “co-polymer,” also known as a “heteropolymer,”is a polymer resulting from polymerization of two or more monomerspecies.

As used herein, the term “copolymerization” refers to the simultaneouspolymerization of two or more monomer species.

As used herein, the term “polymer” generally includes, but is notlimited to homopolymers, co-polymers, such as, for example, block,graft, random and alternating copolymers, and combinations andmodifications thereof.

As used herein, the terms “Continuous Stirred Tank Reactor,”“Continuously Stirred Tank Reactor” and “CSTR,” refer to a tank whichhas a rotor that stirs reagents within the tank to ensure proper mixing,a CSTR can be used for a variety of reactions and processes and isgenerally known in the art.

The various embodiments of the present invention can be joined incombination with other embodiments of the invention and the listedembodiments herein are not meant to limit the invention. Allcombinations of various embodiments of the invention are enabled, evenif not given in a particular example herein.

While illustrative embodiments have been depicted and described,modifications thereof can be made by one skilled in the art withoutdeparting from the spirit and scope of the disclosure. Where numericalranges or limitations are expressly stated, such express ranges orlimitations should be understood to include iterative ranges orlimitations of like magnitude falling within the expressly stated rangesor limitations (e.g., from about 1 to about 10 includes, 2, 3, 4, etc.;greater than 0.10 includes 0.11, 0.12, 0.13, etc.).

Use of the term “optionally” with respect to any element of a claim isintended to mean that the subject element is required, or alternatively,is not required. Both alternatives are intended to be within the scopeof the claim. Use of broader terms such as comprises, includes, having,etc. should be understood to provide support for narrower terms such asconsisting of, consisting essentially of, comprised substantially of,etc.

Depending on the context, all references herein to the “invention” mayin some cases refer to certain specific embodiments only. In other casesit may refer to subject matter recited in one or more, but notnecessarily all, of the claims. While the foregoing is directed toembodiments, versions and examples of the present invention, which areincluded to enable a person of ordinary skill in the art to make and usethe inventions when the information in this patent is combined withavailable information and technology, the inventions are not limited toonly these particular embodiments, versions and examples. Also, it iswithin the scope of this disclosure that the aspects and embodimentsdisclosed herein are usable and combinable with every other embodimentand/or aspect disclosed herein, and consequently, this disclosure isenabling for any and all combinations of the embodiments and/or aspectsdisclosed herein. Other and further embodiments, versions and examplesof the invention may be devised without departing from the basic scopethereof and the scope thereof is determined by the claims that follow.

1. A foamable polystyrene composition comprising: a styrenic co-polymerresulting from polymerization of a reaction mixture comprising astyrenic monomer and a co-monomer comprising a polar functional group.2. The foamable polystyrene composition of claim 1, wherein the styrenicmonomer is selected from the group consisting of styrene, alpha-methylstyrene, vinyl toluene, p-methyl styrene, t-butyl styrene,o-chlorostyrene, vinyl pyridine, and any combinations thereof.
 3. Thefoamable polystyrene composition of claim 1, wherein the co-monomercomprising a polar functional group is present in amounts ranging from0.5 to 10 wt % based on the total weight of the reaction mixture.
 4. Thefoamable polystyrene composition of claim 1, wherein the co-monomercomprising a polar functional group is a polar monomer selected from thegroup consisting of hydroxyethylmethacrylate (HEMA), caprolactoneacrylate, alkyl (meth)acrylate, fluorinated (meth)acrylate,3-(trimethoxysilyl)propyl methacrylate, maleic anhydride and any otherpolymerizable monomers containing polar functionalities such as esters,ethers, carboxylic acids or silanes, and combinations thereof.
 5. Thefoamable polystyrene composition of claim 1, wherein styrene is presentin amounts ranging from 80 to 100 wt % based on the total weight of thepolystyrene copolymers.
 6. The foamable polystyrene composition of claim4, wherein the co-monomer comprising a polar functional group is HEMA.7. The foamable polystyrene composition of claim 1, further comprising ablowing agent.
 8. The foamable polystyrene composition of claim 7,wherein the blowing agent is selected from the group of carbon dioxide(CO₂), water (H₂O), ethanol, air, nitrogen, argon, and helium andcombinations thereof.
 9. The foamable polystyrene composition of claim7, wherein the blowing agent is present in the styrenic co-polymer in aweight proportion ranging from 1 to 30 parts per 100 parts of styrenicmaterial.
 10. A polystyrene foam obtained from the foamable polystyrenecomposition of claim
 1. 11. An article made from the polystyrene foam ofclaim
 10. 12. A method of making a polar polystyrene copolymercomprising: combining a styrene monomer and a polar co-monomer to obtaina reaction mixture; subjecting the reaction mixture to polymerizationconditions to obtain a styrenic co-polymer; and combining the styrenicco-polymer with a blowing agent to obtain a foamable blend.
 13. Themethod of claim 12, wherein the polar co-monomer is selected from thegroup consisting of hydroxyethylmethacrylate (HEMA), caprolactoneacrylate, alkyl (meth)acrylate, fluorinated (meth)acrylate,3-(trimethoxysilyl)propyl methacrylate, maleic anhydride and any otherpolymerizable monomers containing polar functionalities such as esters,ethers, carboxylic acids or silanes, and combinations thereof.
 14. Themethod of claim 12, wherein the polar co-monomer is selected from thegroup consisting of HEMA, caprolactone acrylate and combinationsthereof.
 15. The method of claim 12, wherein the polar co-monomer isadded to the reaction mixture in amounts ranging from 0.5 to 10 wt %based on the total weight of the reaction mixture.
 16. The method ofclaim 12, wherein the blowing agent is selected from the group of carbondioxide (CO₂), water (H₂O), ethanol, air, nitrogen, argon, and heliumand combinations thereof.
 17. The method of claim 12, wherein theblowing agent is added to the styrenic co-polymer in a weight proportionranging from 1 to 30 parts per 100 parts of styrenic material.
 18. Anexpandable polystyrene, comprising: a styrenic copolymer; and a blowingagent; wherein the styrenic polymer results from polymerization of areaction mixture of a styrene monomer and a co-monomer having a polarfunctional group; wherein the co-monomer having a polar functional groupis present in the reaction mixture in amounts of from 0.1 to 10 wt %.19. The expandable polystyrene of claim 18, wherein the co-monomerhaving a polar functional group is selected from the group consisting ofhydroxyethylmethacrylate (HEMA), caprolactone acrylate, alkyl(meth)acrylate, fluorinated (meth)acrylate, 3-(trimethoxysilyl)propylmethacrylate, maleic anhydride and any other polymerizable monomerscontaining polar functionalities such as esters, ethers, carboxylicacids or silanes, and combinations thereof
 20. The expandablepolystyrene of claim 18, wherein the blowing agent is selected from thegroup of carbon dioxide (CO₂), water (H₂O), ethanol, air, nitrogen,argon, and helium and combinations thereof.
 21. The expandablepolystyrene of claim 18, wherein the blowing agent is incorporated intothe expandable polystyrene in a weight proportion ranging from 1 to 30parts per 100 parts of the styrenic material.